Influence of polymerization conditions on the microindentation mechanical properties of poly(allyl(p-allylcarbonate) benzoate)

Abstract

Flat plates of poly(allyl(p-allylcarbonate) benzoate) obtained via photopolymerization and thermal polymerization have been studied by means of microindentation. The plates were about 3 mm thick. The values of microhardness (MHV)/total microhardness (MHT) have been determined. Accordingly, structural changes in the plate bulk due to the polymerization method were detected. The plates obtained by photopolymerization possess a superficial layer harder than the inner layers and its thickness is not uniform.Also, microindentention shows that the increase in the polymerization time during thermopolymerization leads to improved elasticity and resistance against plastic deformation. Microindentation data of the plates here studied shows that poor mechanical properties correspond to an unfinished network, while good mechanical properties correspond to a better crosslinked network. Методом мікроіндентування досліджено плоскі пластини полі(аліл(р-алілкарбонату) бензоату) товщиною біля 3 мм, отримані за допомогою фотополімеризації і термічної полімеризації. Визначено значення мікротвердості до загальної мікротвердості. Відповідно, були виявлені структурні зміни в пластинах в залежності від методу полімеризації. Пластини, отримані фотополімеризацією, мають твердіший поверхневий шар порівняно з внутрішніми шарами і його товщина не є рівномірною. За допомогою мікроіндентування показано, що збільшення часу полімеризації при термополімеризації приводить до поліпшення еластичності та опору до пластичної деформації. Доведено,що недостатні механічні властивості відповідають незавершеній сітці, а непогані – сітці, яка краще зшита.