Chemical modification of ED-24 epoxy resin by adipic acid

Abstract

The possibility of epoxy resin carboxyontaining derivative (CDER) obtaining has been studied on the basis of dianic epoxy resin ED-24 and adipic acid (AA). The synthesized CDER contains epoxy and carboxy groups at the same time. Used catalysts were benzyltriethylammonium chloride (BTEACh); 1,4-diazobicyclo[2,2,2] octane; N,N-dimethylaminopyridine; 18-Crown-6, potassium hydroxide, triethylamine and 18-Crown-6+ZnCl2 catalytic system. The effect of the catalyst nature and amount, reagents ratio, process temperature and time on the reaction proceeding between ED-24 and AA has been determined. The structure of CDER synthesized in the presence of BTEACh and its characterics were confirmed by IR-spectroscopy. Using industrial dianic epoxy resin ED-20 the cross-linking of polymeric composites containing 10, 20 and 30 mass parts of CDER has been investigated at 413 K in the presence of polyethylenepolyamine. Вивчена можливість одержання на основі діанової епоксидної смоли ЕД-24 і адипінової кислоти (АК) карбоксилвмісної похідної епоксидної смоли (КПЕС), яка одночасно містить вільну епоксидну і карбоксильну групу. Встановлено вплив природи та кількості каталізатора, зокрема бензилтриетиламонію хлористого (БТЕАХ), 1,4-діазобіцикло[2,2,2]октану, N,N-диметиламінопіридину, 18-Краун-6, гідроксиду калію, триетиламіну та каталітичної системи 18-Краун-6+ZnCl2, співвідношення реагуючих речовин, температури і тривалості реакції на протікання реакції між ЕД-24 та АК. КПЕС синтезована в присутності як каталізатор БТЕАХ та охарактеризована. ІЧ-спектроскопічними дослідженнями підтверджена структура КПЕС. З використанням промислової діанової епоксидної смоли ЕД-20 вивчено при 413 К структурування у присутності поліетиленполіаміну полімерних сумішей, що містять 10, 20 і 30 мас.част. КПЕС.